AISI H10 /din 1.2365 32CrMoV12-28 h10 jis skd7 steel bar
1.2365 bohler tal-azzar
AZZAR TAL-GĦODDA GĦAL XOGĦOL SĦUN 32CRMOV12-28, 1.2365, AISI H-10 SKOND ISO 4957.
| Standard | Grad tal-Azzar | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Kompożizzjoni Kimika fil-mija | |||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Lu: | V: | ||
| ISO | 1.2365 - 32CrMoV12-28 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.02 | 2.7 - 3.2 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| DIN | 32CrMoV3-3 - 32 CrMoV 3-3 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.7 - 3.2 | 2.6 - 3.0 | 0.4 - 0.7 | ||
| PN | WLV | ||||||||
| 0.25 - 0.35 | 0.25 - 0.50 | 0.15 - 0.40 | <0.03 | <0.03 | 2.5 - 3.0 | 2.5 - 3.0 | 0.4 - 0.6 | ||
| MT | 30CrMoV12-11 | ||||||||
| 0.25 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.5 - 3.5 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| ASTM | AISI H-10 - UNS T20810 | ||||||||
| 0.35 - 0.45 | 0.2 - 0.7 | 0.8 - 1.25 | <0.03 | <0.03 | 3.00 - 3.75 | 2.0 - 3.0 | 0.25 - 0.75 | ||
| GOST | 3H3M3F - | ||||||||
| 0.27 - 0.34 | 0.2 - 0.5 | 0.1 - 0.4 | <0.03 | <0.03 | 2.8 - 3.5 | 2.5 - 3.0 | 0.4 - 0.6 | ||
1.2365, 32CrMoV12-28, X32CrMoV3-3 - speċifikazzjonijiet u applikazzjonijiet
Azzar tal-għodda għax-xogħol sħun, użat għall-produzzjoni ta 'matriċi tal-istampa, inserzjonijiet tad-die, forom għall-ikkastjar ta' metalli mhux tal-ħadid, għodod u timbri għall-ippressar u l-ittimbrar. Huwa kkaratterizzat minn hardenability għolja, konduttività termali eċċellenti, reżistenza għad-differenzi fit-temperatura waqt it-tkessiħ tal-ilma, u reżistenza għat-tempra. Huwa jikseb livelli ta 'ebusija ta' 52 HRC.
Proprjetajiet mekkaniċi tal-azzar 1.2365, 32CrMoV12-28
Ebusija f'kundizzjoni ta' konsenja plus A:<229 HB Hardness in +A+C delivery condition: <249 HB Hardness after hardening: 52 HRC Hardness after hardening and tempering at temperature: 300℃ = 47.2 HRC 350℃ = 47.6 HRC 400℃ = 48.5 HRC 450℃ = 50.0 HRC 500℃ = 51.7 HRC 550℃ = 51.9 HRC 600℃ = 49.0 HRC Thermal conductivity, λ: 36 W * m-1 * K-1 Linear expansion coefficient, α: 12.4 * 10-6 K-1
Trattament bis-sħana tal-azzar 1.2365, 32CrMoV12-28
Trattib ittemprar fi 740 - 770 grad Relief ittemprar fi 600 - 700 grad Tibbies fi 1030 - 1050 grad Ittemprar fi 450 - 550 grad Nitrurazzjoni fi 470 - 550 grad
2.Oqsma ta' Applikazzjoni tal-Prodott:
Il-prodotti tagħna ntużaw f'kull tip ta 'oqsma, bħall-avjazzjoni, l-ajruspazju, in-navigazzjoni, l-enerġija nukleari, l-industrija kimika,
informazzjoni elettronika, manifattura tal-magni, petrokimika, karozzi, strument u arloġġ, Komunikazzjoni, trasport, u strumenti mediċi, eċċ.
3.Grad tal-azzar simili u materjali tal-azzar ekwivalenti:
|
L-Istati Uniti |
Ġappuniż |
Ġemanja |
Brittaniċi |
Franza |
trattament bis-sħana |
Ċiniż |
|
ASTM&AISI&SAE |
JIS |
MT DIN |
MT BS |
MT NF |
ISO |
GB |
|
AISI H10 |
1.2365 |
------ |
||||
1.2365 bohler azzar u bar mill-fabbrika
It-tags Popolari: 1.2365 azzar bohler jis skd7, iċ-Ċina, manifatturi, fornituri, fabbrika