Azzar tond bar 20NiCrMoS6-4 DIN 1.6571
Kompożizzjoni kimika fil-mija tal-analiżi kuċċarina tal-grad tal-azzar: 20NiCrMoS6-4
| 0.16-0.23 | Max 0.40 | 0.50-0.90 | Max 0.035 | 0.020-0.040 | 0.60-0.90 |
| 1.40-1.70 | 0.25-0.35 | ||||
Proċess: EAF flimkien ma LF u VD flimkien ma' Trattament Falsifikat (mhux obbligatorju)
FIRXA TA' DAQS:
Round:
Hot Forged: 50mm-2000mm
Ċatt:
Hot falsifikati: Ħxuna:50-600mm Wisa': sa 1600mm
TERMI TAL-WIĊĊ:
Iswed, Imdawwar & Mitħun
Test: Test ultrasoniku skond SEP 1921-84 C/c, D/d, E/e
Trattament tas-Sħana
Ittemprar, Normalizzar, Tkessiħ, Ittemprar
Proprjetajiet Mekkaniċi
| Proprjetajiet | Kundizzjonijiet | ||
|---|---|---|---|
| T (grad) | Trattament | ||
| Densità (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Proporzjon ta' Poisson | 0.27-0.30 | 25 | |
| Modulu Elastiku (GPa) | 190-210 | 25 | |
| Qawwa tat-tensjoni (Mpa) | 1158 | 25 | żejt imkessaħ, qamħ fin, ittemprat f'425 grad |
| Qawwa tar-Rendiment (Mpa) | 1034 | ||
| Titwil ( fil - mija ) | 15 | ||
| Tnaqqis fl-Erja ( fil - mija ) | 53 | ||
| Ebusija (HB) | 335 | 25 | żejt imkessaħ, qamħ fin, ittemprat f'425 grad |
PROPRJETAJIET TERMALI
| Proprjetajiet | Kundizzjonijiet | ||
|---|---|---|---|
| T (grad) | Trattament | ||
| Konduttività Termali (W/mK) | 42.7 | 100 | |
| Sħana Speċifika (J/kg-K) | 477 | 50-100 | |
PROPRJETAJIET FIŻIĊI
| Kwantità | Valur | Unità |
|---|---|---|
| Espansjoni termali | 16 - 17 | e-6/K |
| Konduttività termali | 16 - 16 | W/m.K |
| Sħana speċifika | 500 - 500 | J/kg.K |
| Temperatura tat-tidwib | 1370 - 1400 | grad |
| Temperatura tas-servizz | 0 - 500 | grad |
| Densità | 8000 - 8000 | kg/m3 |
| Reżistenza | 0.7 - 0.7 | Ohm.mm2/m |
It-tags Popolari: azzar tond bar 20nicrmos6-4 din 1.6571, iċ-Ċina, manifatturi, fornituri, fabbrika